An on-site inspection provided detailed photographic and videotape evidence of undocumented flood damage to manufacturing equipment might otherwise have gone undetected (an insurance investigation related to corrosion damage).
Adhesion tests were performed to test paint bond strength during the on-site inspection.
An on-site building inspection showed paint defects originating from undercutting at the silicone caulked joints due to chemical incompatibility.
Chemical incompatibility of the acrylic topcoat over a silicone joint caused failure of the topcoat and undercutting of the adjacent area.